TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
Tensile Stress,yld,Type I,5 mm/min |
710 |
Kgf/cm2 |
ASTM D 638 |
Tensile Stress,brk,Type I,5 mm/min |
610 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min |
5 |
% |
ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min |
7 |
% |
ASTM D 638 |
Tensile Modulus,50 mm/min |
25400 |
Kgf/cm2 |
ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span |
1070 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min,50 mm span |
26000 |
Kgf/cm2 |
ASTM D 790 |
Taber Abrasion,CS-17,1 kg |
35 |
Mg/1000cy |
SABIC Method |
Tensile Stress,yield,50 mm/min |
70 |
MPa |
ISO 527 |
Tensile Stress,break,50 mm/min |
55 |
MPa |
ISO 527 |
Tensile Strain,yield,50 mm/min |
4 |
% |
ISO 527 |
Tensile Strain,break,50 mm/min |
10 |
% |
ISO 527 |
Tensile Modulus,1 mm/min |
2500 |
MPa |
ISO 527 |
Flexural Stress,yield,2 mm/min |
110 |
MPa |
ISO 178 |
Flexural Modulus,2 mm/min |
2400 |
MPa |
ISO 178 |
Hardness,H358/30 |
113 |
MPa |
ISO 2039-1 |
IMPACT |
Izod Impact, notched,23℃ |
33 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched,-30℃ |
18 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy,23℃ |
509 |
cm-kgf |
ASTM D 3763 |
Izod Impact,notched 80*10*3+23℃ |
13 |
kJ/m2 |
ISO 180/1A |
Izod Impact, notched 80*10*3-30℃ |
5 |
kJ/m2 |
ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm |
14 |
kJ/m2 |
ISO 179/1eA |
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm |
5 |
kJ/m2 |
ISO 179/1eA |
THERMAL |
Vicat Softening Temp,Rate B/50 |
155 |
℃ |
ASTM D 1525 |
HDT/Be,1.82MPa,3.2mm,unannealed |
135 |
℃ |
ASTM D 648 |
CTE,-40℃ to 40℃,flow |
7.5E-05 |
1/℃ |
ASTM E 831 |
CTE,-40℃ to 40℃,xflow |
7.5E-05 |
1/℃ |
ASTM E 831 |
Thermal Conductivity |
0.27 |
W/m-℃ |
ISO 8302 |
CTE,23℃ to 80℃,flow |
7E-05 |
1/℃ |
ISO 11359-2 |
CTE,23℃ to 80℃,xflow |
9E-05 |
1/℃ |
ISO 11359-2 |
Ball Pressure Test,125℃+/-2℃ |
PASSES |
- |
IEC 60695-10-2 |
Ball Pressure Test,approximate maximum |
140 |
℃ |
IEC 60695-10-2 |
Vicat Softening Temp,Rate A/50 |
160 |
℃ |
ISO 306 |
Vicat Softening Temp,Rate B/50 |
145 |
℃ |
ISO 306 |
Vicat Softening Temp,Rate B/120 |
155 |
℃ |
ISO 306 |
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm |
140 |
℃ |
ISO 75/Be |
HDT/Ae,1.8MPa Edgew 120*10*4 sp=100mm |
130 |
℃ |
ISO 75/Ae |
Relative Temp Index,Elec |
110 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
105 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
115 |
℃ |
UL 746B |
PHYSICAL |
Specific Gravity |
1.11 |
-- |
ASTM D 792 |
Mold Shrinkage on Tensile Bar,flow(2) |
0.5-0.7 |
% |
SABIC Method |
Mold Shrinkage, flow.3.2 mm |
0.5-0.7 |
% |
SABIC Method |
Melt Flow Rate,280℃/5.0 kgf |
3.5 |
g/10 min |
ASTM D 1238 |
Density |
1.11 |
g/cm3 |
ISO 1183 |
Water Absorption,(23℃/sat) |
0.18 |
% |
ISO 62 |
Moisture Absorption(23℃/50% RH) |
0.06 |
% |
ISO 62 |
Melt Volume Rate,MVR at 300℃/5.0kgf |
10 |
Cm3/10 min |
ISO 1133 |
ELECTRICAL |
Volume Resistivity |
1E+15 |
Ohm-cm |
IEC 60093 |
Surface Resistivity,ROA |
>1E+15 |
Ohm |
IEC 60093 |
Dielectric Strength,in oil,0.8mm |
33 |
kV/mm |
IEC 60243-1 |
Dielectric Strength,in oil,1.6mm |
26 |
kV/mm |
IEC 60243-1 |
Dielectric Strength,in oil,3.2mm |
16 |
kV/mm |
IEC 60243-1 |
Relative Permittivity,50/60Hz |
2.8 |
- |
IEC 60250 |
Relative Permittivity,1MHz |
2.7 |
- |
IEC 60250 |
Dissipation Factor,50/60 Hz |
0 |
- |
IEC 60250 |
Dissipation Factor, 1MHz |
0.003 |
- |
IEC 60250 |
Comparative Tracking Index |
250 |
V |
IEC 60112 |
FLAME CHARACTERISTICS |
UL Recognized,94V-0 Flame Class Rating(3) |
1.5 |
Mm |
UL 94 |
UL Recognized,94-5VA Rating(3) |
2 |
Mm |
UL 94 |
Glow Wire Flammability Index 960℃,passes at |
1 |
Mm |
IEC 60695-2-12 |
Glow Wire Ignitability Temperature,1.0mm |
775 |
℃ |
IEC 60695-2-13 |
Glow Wire Ignitability Temperature,2.0mm |
775 |
℃ |
IEC 60695-2-13 |
Glow Wire Ignitability Temperature,3.0mm |
775 |
℃ |
IEC 60695-2-13 |
Oxygen Index(LOI) |
32 |
% |
ISO 4589 |