TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
Tensile Stress,yld,Type I,5 mm/min |
590 |
Kgf/cm2 |
ASTM D 638 |
Tensile Stress,brk,Type I,5 mm/min |
620 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min |
6 |
% |
ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min |
130 |
% |
ASTM D 638 |
Tensile Modulus,50 mm/min |
21400 |
Kgf/cm2 |
ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span |
900 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min,50 mm span |
21000 |
Kgf/cm2 |
ASTM D 790 |
Tensile Stress,yield,50 mm/min |
55 |
MPa |
ISO 527 |
Tensile Stress,break,50 mm/min |
60 |
MPa |
ISO 527 |
Tensile Strain,yield,50 mm/min |
6 |
% |
ISO 527 |
Tensile Strain,break,50 mm/min |
125 |
% |
ISO 527 |
Tensile Modulus,1 mm/min |
2100 |
MPa |
ISO 527 |
Flexural Stress,yield,2 mm/min |
85 |
MPa |
ISO 178 |
Flexural Modulus,2 mm/min |
2200 |
MPa |
ISO 178 |
Hardness,H358/30 |
90 |
MPa |
ISO 2039-1 |
IMPACT |
Izod Impact, notched,23℃ |
81 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched,-30℃ |
69 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched,-50℃ |
59 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact, notched,23℃,6.4mm |
65 |
cm-kgf/cm |
ASTM D 256 |
Izod Impact,double-gated,23℃ |
108 |
cm-kgf/cm |
SABIC Method |
Instrumented Impact Total Energy,23℃ |
539 |
cm-kgf |
ASTM D 3763 |
Izod Impact,unnotched 80*10*3+23℃ |
NB |
kJ/m2 |
ISO 180/1U |
Izod Impact,unnotched 80*10*3-30℃ |
NB |
kJ/m2 |
ISO 180/1U |
Izod Impact,notched 80*10*3+23℃ |
70 |
kJ/m2 |
ISO 180/1A |
Izod Impact, notched 80*10*3-30℃ |
55 |
kJ/m2 |
ISO 180/1A |
Izod Impact, notched 63.5*12.7*3.2,23℃ |
80 |
kJ/m2 |
ISO 180/4A |
Izod Impact, notched 63.5*12.7*3.2,-30℃ |
65 |
kJ/m2 |
ISO 180/4A |
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm |
75 |
kJ/m2 |
ISO 179/1eA |
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm |
60 |
kJ/m2 |
ISO 179/1eA |
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m2 |
ISO 179/1eU |
Charpy -30℃, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m2 |
ISO 179/1eU |
THERMAL |
Vicat Softening Temp,Rate B/50 |
142 |
℃ |
ASTM D 1525 |
HDT/Be,0.45MPa,3.2mm,unannealed |
134 |
℃ |
ASTM D 648 |
HDT/Be,1.82MPa,3.2mm,unannealed |
120 |
℃ |
ASTM D 648 |
HDT/Be,1.82MPa,6.4mm,unannealed |
124 |
℃ |
ASTM D 648 |
CTE,-40℃ to 40℃,flow |
6.66E-05 |
1/℃ |
ASTM E 831 |
CTE,-40℃ to 40℃,xflow |
6.66E-05 |
1/℃ |
ASTM E 831 |
CTE,23℃ to 80℃,flow |
7.2E-05 |
1/℃ |
ISO 11359-2 |
CTE,23℃ to 80℃,xflow |
7.7E-05 |
1/℃ |
ISO 11359-2 |
Ball Pressure Test,125℃+/-2℃ |
PASSES |
- |
IEC 60695-10-2 |
Vicat Softening Temp,Rate B/50 |
140 |
℃ |
ISO 306 |
Vicat Softening Temp,Rate B/120 |
142 |
℃ |
ISO 306 |
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm |
135 |
℃ |
ISO 75/Be |
HDT/Ae,1.8MPa Edgew 120*10*4 sp=100mm |
124 |
℃ |
ISO 75/Ae |
Relative Temp Index,Elec |
125 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
115 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
120 |
℃ |
UL 746B |
PHYSICAL |
Specific Gravity |
1.18 |
- |
ASTM D 792 |
Mold Shrinkage, flow.3.2 mm |
0.4-0.8 |
% |
SABIC Method |
Mold Shrinkage,xflow.3.2 mm |
0.4-0.8 |
% |
SABIC Method |
Melt Flow Rate,300℃/1.2 kgf |
10 |
g/10 min |
ASTM D 1238 |
Density |
1.19 |
g/cm3 |
ISO 1183 |
Water Absorption,(23℃/sat) |
0.35 |
% |
ISO 62 |
Moisture Absorption(23℃/50% RH) |
0.15 |
% |
ISO 62 |
Melt Volume Rate,MVR at 300℃/1.2kgf |
9 |
Cm3/10 min |
ISO 1133 |
ELECTRICAL |
Dielectric Strength,in oil,3.2mm |
17 |
kV/mm |
ASTM D 149 |
Relative Permittivity,50/60Hz |
2.95 |
- |
ASTM D 150 |
Relative Permittivity,1MHz |
2.9 |
- |
ASTM D 150 |
Dissipation Factor,50/60 Hz |
0.0024 |
- |
ASTM D 150 |
Dissipation Factor, 1MHz |
0.0085 |
- |
ASTM D 150 |
Hot Wire Ignition {PLC} |
1 |
PLC Code |
UL 746A |
High Ampere Arc Ign,surface {PLC} |
0 |
PLC Code |
UL 746A |
Comparative Tracking Index(UL) {PLC} |
3 |
PLC Code |
UL 746A |
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
Surface Resistivity,ROA |
>1.E+15 |
Ohm |
IEC 60093 |
Dielectric Strength,in oil,3.2mm |
16 |
kV/mm |
IEC 60243-1 |
Relative Permittivity,50/60Hz |
2.6 |
- |
IEC 60250 |
Relative Permittivity,1MHz |
2.7 |
- |
IEC 60250 |
Dissipation Factor,50/60 Hz |
0.001 |
- |
IEC 60250 |
Dissipation Factor,1 MHz |
0.008 |
- |
IEC 60250 |
Comparative Tracking Index |
225 |
V |
IEC 60112 |
FLAME CHARACTERISTICS |
UL Recognized,94V-0 Flame Class Rating(3) |
1.49 |
Mm |
UL 94 |
UL Recognized,94-5VA Rating(3) |
2.99 |
Mm |
UL 94 |
Glow Wire Flammability Index 960℃,passes at |
1 |
Mm |
IEC 60695-2-12 |
Glow Wire Ignitability Temperature,1.0mm |
825 |
℃ |
IEC 60695-2-13 |
Oxygen Index(LOI) |
35 |
% |
ISO 4589 |
UV-light,water exposure/immersion |
F1 |
- |
UL 746C |