TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
Tensile Stress,yld,Type I,5 mm/min |
570 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min |
5 |
% |
ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min |
150 |
% |
ASTM D 638 |
Tensile Modulus,50 mm/min |
22400 |
Kgf/cm2 |
ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span |
870 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min,50 mm span |
23900 |
Kgf/cm2 |
ASTM D 790 |
IMPACT |
Izod Impact, notched,23℃ |
65 |
cm- kgf/cm |
ASTM D 256 |
Izod Impact,notched,-30℃ |
54 |
cm- kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy, 23℃ |
553 |
cm- kgf |
ASTM D 3763 |
Instrumented Impact Total Energy, -30℃ |
414 |
cm- kgf |
ASTM D 3763 |
THERMAL |
HDT/Be,0.45MPa,3.2mm,unannealed |
123 |
℃ |
ASTM D 648 |
HDT/Be,1.82MPa, 3.2mm,unannealed |
107 |
℃ |
ASTM D 648 |
CTE,-40℃ to 40℃,flow |
7.2E-05 |
1/℃ |
ASTM E 831 |
Thermal Conductivity |
0.2 |
W/m-℃ |
ASTM C 177 |
Relative Temp Index,Elec |
60 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
60 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
60 |
℃ |
UL 746B |
PHYSICAL |
Specific Gravity |
1.14 |
- |
ASTM D 792 |
Water Absorption,24 hours |
0.1 |
% |
ASTM D 570 |
Water Absorption,equilibrium,23C |
0.4 |
% |
ASTM D 570 |
Mold Shrinkage,flow,3.2mm |
0.5-0.7 |
% |
SABIC Method |
Melt Flow Rate,230℃/3.8kgf |
2.5 |
g/10 min |
ASTM D 1238 |
Melt Flow Rate,260℃/3.8kgf |
8 |
g/10 min |
ASTM D 1238 |
ELECTRICAL |
Arc Resistance,Tungstem{PLC} |
5 |
PLC Code |
ASTM D 495 |
Hot Wire Ignition{PLC} |
3 |
PLC Code |
UL 746A |
High Voltage Arc Track Rate{PLC} |
1 |
PLC Code |
UL 746A |
High Ampere Arc Ign,surface{PLC} |
0 |
PLC Code |
UL 746A |
Comparative Tracking Idex(UL) {PLC} |
3 |
PLC Code |
UL 746A |
FLAME CHARACTERISTICS |
UL Recognized,94HB Flame Class Rating(3) |
1.21 |
Mm |
UL 94 |
CSA(See File for complete listing) |
LS88480 |
File No. |
CSA LISTED |
UV-light,water exposure/immersion |
F2 |
- |
UL 746C |
PROCESSING PARAMETERS |
TYPICAL VALUE |
UNIT |
Injection Molding |
Drying Temperature |
105-110 |
℃ |
Drying Time |
3-4 |
Hrs |
Drying Time(Cumulative) |
8 |
Hrs |
Maximum Moisture Content |
0.04 |
% |
Melt Temperature |
275-300 |
℃ |
Nozzle Temperature |
275-300 |
℃ |
Front-Zone 3 Temperature |
260-300 |
℃ |
Middle-Zone 2 Temperature |
255-295 |
℃ |
Rear-Zone 1 Temperature |
250-290 |
℃ |
Mold Temperature |
60-90 |
℃ |
Back Pressure |
0.3-0.7 |
MPa |
Screw Speed |
40-70 |
Rpm |
Shot to Cylinder Size |
30-80 |
% |
Vent Depth |
0.038-0.076 |
Mm |
|
|