TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
Tensile Stress,yld,Type I,5 mm/min |
630 |
Kgf/cm2 |
ASTM D 638 |
Tensile Stress,brk,Type I,5 mm/min |
680 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min |
6 |
% |
ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min |
125 |
% |
ASTM D 638 |
Tensile Modulus,50 mm/min |
23100 |
Kgf/cm2 |
|
Flexural Stress,yld,1.3 mm/min,50 mm span |
1020 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min,50 mm span |
24100 |
Kgf/cm2 |
ASTM D 790 |
IMPACT |
Izod Impact,notched,23℃ |
81 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Total Energy,23℃ |
805 |
cm-kgf |
ASTM D 3763 |
THERMAL |
Vicat Softening Temp,Rate B/50 |
143 |
℃ |
ASTM D 1525 |
HDT/Be,0.45MPa,3.2mm,unannealed |
137 |
℃ |
ASTM D 648 |
HDT/Be,1.82MPa,3.2mm,unannealed |
126 |
℃ |
ASTM D 648 |
CTE,-40℃ to 40℃,flow |
6.84E-05 |
1/℃ |
ASTM E 831 |
CTE,-40℃ to 40℃,xflow |
7.38E-05 |
1/℃ |
ASTM E 831 |
Relative Temp Index,Elec |
130 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
120 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
130 |
℃ |
UL 746B |
PHYSICAL |
Specific Gravity |
1.19 |
- |
ASTM D 792 |
Mold Shrinkage,flow,3.2mm |
0.6-0.8 |
% |
SABIC Method |
Melt Flow Rate,300℃/1.2kgf |
10 |
g/10 min |
ASTM D 1238 |
ELECTRICAL |
Arc Resistance,Tungsten {PLC} |
7 |
PLC Code |
ASTM D 495 |
Hot Wire Ignition {PLC} |
2 |
PLC Code |
UL 746A |
High Voltage Arc Track Rate {PLC} |
3 |
PLC Code |
UL 746A |
High Ampere Arc Ign,surface {PLC} |
3 |
PLC Code |
UL 746A |
Comparative Tracking Index(UL) {PLC} |
2 |
PLC Code |
UL 746A |
FLAME CHARACTERISTICS |
UL Recognized,94V-2 Flame Class Rating(3) |
0.8 |
Mm |
UL 94 |
UL Recognized,94V-0 Flame Class Rating(3) |
3.04 |
Mm |
UL 94 |
Glow Wire Flammability Index 960℃,passes at |
1 |
Mm |
IEC 60695-2-12 |
Glow Wire Ignitability Temperature,1.0mm |
850 |
℃ |
IEC 60695-2-13 |
Oxygen Index(LOI) |
35 |
% |
ISO 4589 |
PROCESSING PARAMETERS |
TYPICAL VALUE |
UNIT |
Injection Molding |
Drying Temperature |
120 |
℃ |
Drying Time |
2-4 |
Hrs |
Maximum Moisture Content |
0.02 |
% |
Melt Temperature |
280-310 |
℃ |
Nozzle Temperature |
270-290 |
℃ |
Front-Zone 3 Temperature |
280-310 |
℃ |
Middle-Zone 2 Temperature |
270-290 |
℃ |
Rear-Zone 1 Temperature |
260-280 |
℃ |
Hopper Temperature |
60-80 |
℃ |
Mold Temperature |
80-110 |
℃ |
|
|