TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
Tensile Stress,yld,Type I,5 mm/min |
630 |
Kgf/cm2 |
ASTM D 638 |
Tensile Stress,brk,Type I,5 mm/min |
560 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min |
7 |
% |
ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min |
90 |
% |
ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span |
920 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min,50 mm span |
22800 |
Kgf/cm2 |
ASTM D 790 |
Hardness,Rockwell M |
70 |
- |
ASTM D 785 |
Hardness,Rockwell R |
118 |
- |
ASTM D 785 |
Taber Abrasion,CS-17,1 kg |
10 |
Mg/1000cy |
ASTM D 1044 |
IMPACT |
Izod Impact,unnotched,23℃ |
326 |
cm-kgf/cm |
ASTM D 4812 |
Izod Impact,notched,23℃ |
65 |
cm-kgf/cm |
ASTM D 256 |
Tensile Impact,Type “S” |
535 |
cm-kgf/cm2 |
ASTM D 1822 |
Falling Dart Impact(D 3029),23℃ |
1728 |
cm-kgf |
ASTM D 3029 |
THERMAL |
Vicat Softening Temp,Rate B/50 |
151 |
℃ |
ASTM D 1525 |
HDT/Be,0.45MPa,6.4mm,unannealed |
137 |
℃ |
ASTM D 648 |
HDT/Be,1.82MPa,6.4mm,unannealed |
132 |
℃ |
ASTM D 648 |
CTE,-40℃ to 95℃,flow |
6.84E-05 |
1/℃ |
ASTM E 831 |
Thermal Conductivity |
0.19 |
W/m-℃ |
ASTM C 177 |
Relative Temp Index,Elec |
130 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
120 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
130 |
℃ |
UL 746B |
PHYSICAL |
Specific Gravity |
1.21 |
- |
ASTM D 792 |
Specific Volume |
0.83 |
cm3/g |
ASTM D 792 |
Density |
1.217 |
g/cm3 |
ASTM D 792 |
Water Absorption,24 hours |
0.15 |
% |
ASTM D 570 |
Water Absorption,equilibrium,23℃ |
0.35 |
% |
ASTM D 570 |
Water Absorption,equilibrium,100℃ |
0.58 |
% |
ASTM D 570 |
Mold Shrinkage,flow,3.2mm |
0.5-0.7 |
% |
SABIC Method |
Melt Flow Rate,300℃/1.2kgf |
10 |
g/10 min |
ASTM D 1238 |
OPTICAL |
Light Transmission |
85 |
% |
ASTM D 1003 |
Haze |
1 |
% |
ASTM D 1003 |
Refractive Index |
1.586 |
- |
ASTM D 542 |
ELECTRICAL |
Volume Ressistivity |
>1.E+17 |
Ohm-cm |
ASTM D 257 |
Dielectric Strength,in air,3.2mm |
16.7 |
kV/mm |
ASTM D 149 |
Relative Permittivity,50/60Hz |
3.01 |
- |
ASTM D 150 |
Relative Permittivity,1MHz |
2.96 |
- |
ASTM D 150 |
Dissipation Factor,50/60 Hz |
0.0009 |
- |
ASTM D 150 |
Dissipation Factor, 1MHz |
0.01 |
- |
ASTM D 150 |
Arc Resistance,Tungsten {PLC} |
7 |
PLC Code |
ASTM D 495 |
Hot Wire Ignition {PLC} |
2 |
PLC Code |
UL 746A |
High Voltage Arc Track Rate {PLC} |
3 |
PLC Code |
UL 746A |
High Ampere Arc Ign,surface {PLC} |
2 |
PLC Code |
UL 746A |
Comparative Tracking Index(UL) {PLC} |
3 |
PLC Code |
UL 746A |
FLAME CHARACTERISTICS |
UL Recognized,94V-0 Flame Class Rating(3) |
1.47 |
Mm |
UL 94 |
UL Recognized,94-5VA Rating(3) |
2.99 |
Mm |
UL 94 |
Oxygen Index(LOI) |
35 |
% |
ASTM D 2863 |
UV-light,water exposure/immersion |
F1 |
- |
UL 746C |
PROCESSING PARAMETERS |
TYPICAL VALUE |
UNIT |
Injection Molding |
Drying Temperature |
120 |
℃ |
Drying Time |
3-4 |
Hrs |
Drying Time(Cumulative) |
48 |
Hrs |
Maximum Moisture Content |
0.02 |
% |
Melt Temperature |
295-315 |
℃ |
Nozzle Temperature |
290-310 |
℃ |
Front-Zone 3 Temperature |
295-315 |
℃ |
Middle-Zone 2 Temperature |
280-305 |
℃ |
Rear-Zone 1 Temperature |
270-295 |
℃ |
Mold Temperature |
70-95 |
℃ |
Back Pressure |
0.3-0.7 |
MPa |
Screw Speed |
40-70 |
Rpm |
Shot to Cylinder Size |
40-60 |
% |
Vent Depth |
0.025-0.076 |
Mm |
|
|