TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
|
|
|
Tensile Stress,yld,Type I,50 mm/min |
590 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min |
30 |
% |
ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span |
940 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus, 1.3 mm/min,50 mm span |
24600 |
Kgf/cm2 |
ASTM D 790 |
IMPACT |
|
|
|
Izod Impact, notched,23℃ |
21 |
cm- kgf/cm |
ASTM D 256 |
Izod Impact,notched,-40℃ |
13 |
cm- kgf/cm |
ASTM D 256 |
THERMAL |
|
|
|
HDT,1.82MPa,3.2mm,unannealed |
117 |
℃ |
ASTM D 648 |
HDT, 1.82MPa,6.4mm,unannealed |
126 |
℃ |
ASTM D 648 |
CTE,-40℃ to 60℃,flow |
1.3E-04 |
1/℃ |
ASTM E 831 |
Relative Temp Index,Elec |
105 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
90 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
105 |
℃ |
UL 746B |
PHYSICAL |
|
|
|
Specific Gravity |
1.08 |
- |
ASTM D 792 |
Water Absorption,24 hours |
0.06 |
% |
ASTM D 570 |
Mold Shrinkage,flow,3.2mm(5) |
0.5-0.7 |
% |
SABIC Method |
ELECTRICAL |
|
|
|
Dissipation Factor,50/60 Hz |
2.65 |
- |
ASTM D 150 |
PROCESSING PARAMETERS |
TYPICAL VALUE |
UNIT |
Injection Molding |
|
|
Drying Temperature |
105-110 |
℃ |
Drying Time |
2-4 |
Hrs |
Drying Time(Cumulative) |
8 |
Hrs |
Melt Temperature |
280-310 |
℃ |
Mold Temperature |
70-95 |
℃ |
|
|