TYPICAL PROPERTIES |
TYPICAL VALUE |
UNIT |
STANDARD |
MECHANICAL |
Taber Abrasion,CS-17,1kg |
17 |
Mg/1000cy |
SABIC Method |
Tensile Stress,break,5 mm/min |
90 |
MPa |
ISO 527 |
Tensile Strain,break,5 mm/min |
2 |
% |
ISO 527 |
Tensile Modulus,1 mm/min |
6000 |
MPa |
ISO 527 |
Flexural Stress,break,2 mm/min |
120 |
MPa |
ISO 178 |
Flexural Modulus,2 mm/min |
5500 |
MPa |
ISO 178 |
Hardness,H358/30 |
125 |
MPa |
ISO 2039-1 |
IMPACT |
Izod Impact,unnotched 80*10*3+23℃ |
35 |
KJ/M2 |
ISO 180/1U |
Izod Impact,unnotched 80*10*3-30℃ |
35 |
KJ/M2 |
ISO 180/1U |
Izod Impact,notched 80*10*3+23℃ |
7 |
KJ/M2 |
ISO 180/1A |
Izod Impact, notched 80*10*3-30℃ |
6 |
KJ/M2 |
ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm |
6 |
KJ/M2 |
ISO 179/1eA |
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm |
5 |
KJ/M2 |
ISO 179/1eA |
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm |
40 |
KJ/M2 |
ISO 179/1eU |
Charpy -30℃,Unnotch Edgew 80*10*3 sp=62mm |
40 |
KJ/M2 |
ISO 179/1eU |
Charpy Impact,notched,23℃ |
9 |
KJ/M2 |
ISO 179/2C |
THERMAL |
Thermal Conductivity |
0.22 |
W/m-℃ |
ISO 8302 |
CTE,23℃ to80℃,flow |
3E-05 |
1/℃ |
ISO 11359-2 |
Ball Pressure Test,125℃+/-2℃ |
PASSES |
- |
IEC 60695-10-2 |
Vicat Softening Temp,Rate A/50 |
155 |
℃ |
ISO 306 |
Vicat Softening Temp,Rate B/50 |
147 |
℃ |
ISO 306 |
Vicat Softening Temp,Rate B/120 |
145 |
℃ |
ISO 306 |
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm |
144 |
℃ |
ISO 75/Be |
HDT/Ae,1.8MPa Edgew 120*10*4 sp=100mm |
139 |
℃ |
ISO 75/Ae |
Relative Temp Index,Elec |
130 |
℃ |
UL 746B |
Relative Temp Index,Mech w/impact |
125 |
℃ |
UL 746B |
Relative Temp Index, Mech w/o impact |
130 |
℃ |
UL 746B |
PHYSICAL |
Mold Shrinkage on Tensile Bar,Flow(2) |
0.2-0.5 |
% |
SABIC Method |
Density |
1.35 |
g/cm3 |
ISO 1183 |
Water Absorption,(23℃/sat) |
0.29 |
% |
ISO 62 |
Moisture A Absorption(23℃/50% RH) |
0.12 |
% |
ISO 62 |
Melt Volume Rate,MVR at 300℃/1.2kg |
6 |
Cm3/10 min |
ISO 1133 |
OPTICAL |
Haze |
NA |
% |
ASTM D 1003 |
Refractive Index |
NA |
- |
ISO 489 |
ELECTRICAL |
Volume Ressistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
Surface Resistivity,ROA |
>1.E+15 |
Ohm |
IEC 60093 |
Dielectric Strength,shorttime,1.0mm |
20 |
kV/mm |
IEC 60243-1 |
Dielectric Strength,in oil,0.8mm |
33 |
kV/mm |
IEC 60243-1 |
Dielectric Strength,in oil,1.6mm |
25 |
kV/mm |
IEC 60243-1 |
Dielectric Strength,in oil,3.2mm |
16 |
kV/mm |
IEC 60243-1 |
Relative Permittivity,50/60Hz |
3 |
- |
IEC 60250 |
Relative Permittivity,1 MHz |
2.9 |
- |
IEC 60250 |
Dissipation Factor,50/60 Hz |
0.001 |
- |
IEC 60250 |
Dissipation Factor,1 MHz |
0.01 |
- |
IEC 60250 |
Comparative Tracking Index |
150 |
V |
IEC 60112 |
FLAME CHARACTERISTICS |
UL Recognized,94V-0 Flame Class Rating(3) |
1.5 |
Mm |
UL94 |
Glow Wire Flammability Index 850℃,passes at |
1 |
mm |
IEC 60695-2-12 |
Glow Wire Flammability Index 960℃,passes at |
1.6 |
Mm |
IEC 60695-2-12 |
Oxygen Index(LOI) |
37 |
% |
ISO 4589 |