| TYPICAL PROPERTIES1
| TYPICAL VALUE
| Unit
| Standard |
| MECHANICAL |
Tensile Stress, brk, Type I, 50 mm/min
| 230
| kgfc/m2
| ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min
| 85
| %
| ASTM D 638 |
| Flexural Modulus, 12.5 mm/min, 100 mm span
| 6600
| kgfc/m2
| ASTM D 790 |
| Tensile Stress, break, 50 mm/min
| 23
| MPa
| ISO 527 |
| Tensile Strain, break, 50 mm/min
| 90
| %
| ISO 527 |
| Flexural Modulus, 12.5 mm/min
| 720
| MPa
| ISO 178 |
| Hardness, Shore D
| 56
| - | ISO 868 |
| Tear strength
| 25
| N/mm
| ISO 6383 |
| IMPACT |
Brittleness Temperature
| <-40
| °C
| ASTM D 746 |
| THERMAL |
HDT, 0.45 MPa, 6.4 mm, unannealed
| 85
| °C
| ASTM D 648 |
| Vicat Softening Temp, Rate A/50
| 102
| °C
| ISO 306 |
| PHYSICAL |
| Specific Gravity
| 1.03
| -
| ASTM D 792 |
| Water Absorption, 23°C/48hrs
| 0.1
| %
| ASTM D 570 |
| Melt Flow Rate, 250°C/10.0 kgf
| 5.1
| g/10 min
| ASTM D 1238 |
| ELECTRICAL |
| Volume Resistivity
| 3.9E+16
| Ohm-cm
| IEC 60093 |
| Dielectric strength in oil, 2.0mm
| 26
| kV/mm
| IEC 60243-1 |
| Relative Permittivity, 50/60 Hz
| 2.6
| -
| IEC 60250 |
| Relative Permittivity, 1 MHz
| 2.5
| -
| IEC 60250 |
| Dissipation Factor, 50/60 Hz
| 0.024
| -
| IEC 60250 |
| Dissipation Factor, 1 MHz
| 0.003
| -
| IEC 60250 |
| Comparative Tracking Index
| 600
| V
| IEC 60112 |
| TYPICAL PROPERTIES1 |
TYPICAL VALUE |
Unit |
Standard |
| FLAME CHARACTERISTICS |
Smoke Density on 0.5mm plaque, Non-flame, Ds, max |
75 |
- |
ASTM E 662 |
| Smoke Density on 0.5mm plaque, Flame, Ds, max |
150 |
- |
ASTM E 662 |
| Glow Wire Flammability Index 960°C, passes at |
3 |
mm |
IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 3.0 mm |
750 |
°C |
IEC 60695-2-13 |
| Oxygen Index (LOI) |
25 |
% |
ISO 4589 |
| WIRE AND CABLE - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper |
Tensile strength @ break |
33 |
MPa |
UL 1581 |
| Tensile elongation @ break |
197 |
% |
UL 1581 |
| Tensile strength @ break after 7days @136°C |
36 |
MPa |
UL 1581 |
| Tensile elongation @ break after 7days @136°C |
156 |
% |
UL 1581 |
| UL temperature rating |
105 |
°C |
UL 1581 |
Heat Deformation at 121°C/250g |
26 |
% |
UL 1581 |
| VW-1 |
Pass |
- |
UL 1581 |
| PROCESSING PARAMETERS |
TYPICAL VALUE |
UNIT |
| Wire Coating Extrusion |
| Drying Temperature |
60 - 80 |
°C |
| Drying Time |
4-6 |
hrs |
| Drying Time (Cumulative) |
12 |
hrs |
| Maximum Moisture Content |
0.02 |
% |
| Extruder Length/Diameter Ratio (L/D) |
22:1 to 26:1 |
- |
| Screw Speed |
15 - 40 |
rpm |
| Feed Zone Temperature |
210 - 260 |
°C |
| Middle Zone Temperatures |
230 - 285 |
°C |
| Head Zone Temperature |
250 - 285 |
°C |
| Neck Temperature |
250 - 285 |
°C |
| Cross-head Temperature |
250 - 285 |
°C |
| Die Temperature |
250 - 285 |
°C |
| Melt Temperature |
250 - 285 |
°C |
| Conductor Pre-heat Temperature |
80 - 150 |
°C |
| Screen Pack |
150 - 100 |
- |
| Cooling Water Air Gap |
100 - 200 |
mm |
| Water Bath Temperature |
15 - 80 |
°C |
|
|