TYPICAL PROPERTIES |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress,yld Type I,50 mm/min |
640 |
Kgf/cm2 |
ASTM D 638 |
Tensile Strain,yld Type I,50 mm/min |
6 |
% |
ASTM D 638 |
Tensile Strain,brk Type I,50 mm/min |
>70 |
% |
ASTM D 638 |
Tensile Modulus,50 mm/min |
23900 |
Kgf/cm2 |
ASTM D 638 |
Flexural Stress,yld,1.3mm/min,50 mm span |
910 |
Kgf/cm2 |
ASTM D 790 |
Flexural Modulus,1.3mm/min,50 mm span |
23400 |
Kgf/cm2 |
ASTM D 790 |
Hardness,Rockwell R |
120 |
- |
ASTM D 785 |
Tensile Stress,yield,50 mm/min |
63 |
MPa |
ISO 527 |
Tensile Strain,yield,50 mm/min |
6 |
% |
ISO 527 |
Tensile Strain,break,50 mm/min |
>70 |
% |
ISO 527 |
Tensile Modulus,1 mm/min |
2350 |
MPa |
ISO 527 |
Flexural Stress,yield,2 mm/min |
90 |
MPa |
ISO 178 |
Flexural Modulus,2 mm/min |
2300 |
MPa |
ISO 178 |
Hardness,Rockwell R |
120 |
- |
ISO 2039-2 |
IMPACT |
Value |
Unit |
Standard |
Izod Impact,unnotched,23℃ |
NB |
cm-kgf/cm |
ASTM D 4812 |
Izod Impact,notched,23℃ |
81 |
cm-kgf/cm |
ASTM D 256 |
Instrumented Impact Energy @ peak,23℃ |
662 |
cm-kgf |
ASTM D 3763 |
Izod Impact,unnotched 80*10*3+23℃ |
NB |
KJ/m2 |
ISO 180/1U |
Izod Impact,unnotched 80*10*3-30℃ |
NB |
KJ/m2 |
ISO 180/1U |
Izod Impact,notched 80*10*3+23℃ |
70 |
KJ/m2 |
ISO 180/1A |
Izod Impact,notched 80*10*3-30℃ |
12 |
KJ/m2 |
ISO 180/1A |
THERMAL |
Value |
Unit |
Standard |
Vicat Softening Temp,Rate B/50 |
143 |
℃ |
ASTM D 1525 |
HDT,0.45 MPa,3.2mm |
138 |
℃ |
ASTM D 648 |
HDT,1.82MPa,3.2mm |
127 |
℃ |
ASTM D 648 |
CTE,-40℃to 95℃,flow |
7.E-05 |
1/℃ |
ASTM E 831 |
Thermal Conductivity |
0.2 |
W/m-℃ |
ASTM C 177 |
Thermal Conductivity |
0.2 |
W/m-℃ |
ISO 8302 |
CTE,23℃to80℃,flow |
7.E-05 |
1/℃ |
ISO 11359-2 |
Ball Pressure Test,125℃+/-2℃ |
Passes |
- |
IEC 60695-10-2 |
Vicat Softening Temp,Rate B/50 |
143 |
℃ |
ISO 306 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
138 |
℃ |
ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
127 |
℃ |
ISO 75/Af |
PHYSICAL |
Value |
Unit |
Standard |
Specific Gravity |
1.2 |
- |
ASTM D 792 |
Water Absorption,equilibrium,23C |
0.35 |
% |
ASTM D 570 |
Mold Shrinkage on Tensile Bar,flow(2)(5) |
0.5-0.7 |
% |
SABIC Method |
Mold Shrinkage,flow,3.2mm(5) |
0.5-0.7 |
% |
SABIC Method |
Melt Flow Rate,300℃/1.2kgf |
10 |
g/10 min |
ASTM D 1238 |
Density |
1.2 |
g/cm3 |
ISO 1183 |
Water Absorption,( 23℃/sat) |
0.35 |
% |
ISO 62 |
Melt Volume Rate,MVR at 300℃/1.2kg |
9 |
Cm3/10 min |
ISO 1133 |
OPTICAL |
Value |
Unit |
Standard |
Light Transmission,2.54mm |
80-90 |
% |
ASTM D 1003 |
Haze,2.54mm |
<0.8 |
% |
ASTM D 1003 |
Refractive Index |
1.586 |
- |
ASTM D 542 |
Refractive Index |
1.586 |
- |
ISO 489 |
ELECTRICAL |
Value |
Unit |
Standard |
Volume Resistivity |
>1.E+15 |
Ohm-cm |
ASTM D 257 |
Dielectric Strength,1.6mm |
27 |
kV/mm |
ASTM D 149 |
Relative Permittivity,60 Hz |
3 |
- |
ASTM D 150 |
Relative Permittivity,1 MHz |
3 |
- |
ASTM D 150 |
Dissipation Factor,60 Hz |
0.001 |
- |
ASTM D 150 |
Dissipation Factor,1 MHz |
0.01 |
- |
ASTM D 150 |
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
Dielectric Strength,1.6mm |
27 |
kV/mm |
IEC 60243-1 |
Relative Permittivity,60 Hz |
3 |
- |
IEC 60250 |
Relative Permittivity,1 MHz |
3 |
- |
IEC 60250 |
Dissipation Factor,60 Hz |
0.001 |
- |
IEC 60250 |
Dissipation Factor, 1 MHz |
0.01 |
- |
IEC 60250 |
FLAME CHARACERISTICS |
Value |
Unit |
Standard |
UL Recognized,94V-2 Flame Class Rating(3) |
1.6 |
mm |
UL 94 |
Parameter |
Injection Molding |
Value |
Unit |
Drying Temperature |
120 |
℃ |
Drying Time |
2-4 |
Hrs |
Maximum Moisture Content |
0.02 |
% |
Melt Temperature |
280-310 |
℃ |
Nozzle Temperature |
270-290 |
℃ |
Front – Zone 3 Temperature |
280-310 |
℃ |
Middle – Zone 2 Temperature |
270-290 |
℃ |
Rear – Zone 1 Temperature |
260-280 |
℃ |
Hopper Temperature |
60-80 |
℃ |
Mold Temperature |
80-110 |
℃ |
|
|