TYPICAL PROPERTIES1 |
MECHANICAL |
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min |
45 |
MPa |
ISO 527 |
Tensile Stress, brk, Type I, 50 mm/min |
40 |
MPa |
ISO 527 |
Tensile Strain, yld, Type I, 50 mm/min |
3 |
% |
ISO 527 |
Tensile Strain, brk, Type I, 50 mm/min |
30 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
2200 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
60 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2000 |
MPa |
ISO 178 |
Hardness, H358/30 |
95 |
MPa |
ISO 2039-1 |
IMPACT |
Value |
Unit |
Standard |
Izod Impact, notched 80*10*4 +23°C |
11 |
kJ/m2 |
ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C |
5 |
kJ/m2 |
ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
11 |
kJ/m2 |
ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm |
5 |
kJ/m2 |
ISO 179/1eA |
THERMAL |
Value |
Unit |
Standard |
Thermal Conductivity |
0.22 |
W/m-°C |
ISO 8302 |
CTE, 23°C to 80°C, flow |
7.E-05 |
1/°C |
ISO 11359-2 |
CTE, 23°C to 80°C, xflow |
9.E-05 |
1/°C |
ISO 11359-2 |
Ball Pressure Test, 75°C +/- 2°C |
PASSES |
- |
IEC 60695-10-2 |
Ball Pressure Test, approximate maximum |
115 |
°C |
IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 |
120 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/50 |
115 |
°C |
ISO 306 |
Vicat Softening Temp, Rate B/120 |
115 |
°C |
ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
105 |
°C |
ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
95 |
°C |
ISO 75/Ae |
Relative Temp Index, Elec |
90 |
°C |
UL 746B |
Relative Temp Index, Mech w/impact |
85 |
°C |
UL 746B |
Relative Temp Index, Mech w/o impact |
95 |
°C |
UL 746B |
| PHYSICAL |
Value |
Unit |
Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) |
0.5 - 0.7 |
% |
SABIC Method |
| Density |
1.05 |
g/cm3 |
ISO 1183 |
| Water Absorption, (23°C/sat) |
0.2 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
0.07 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 280°C/3.8 kg |
15 |
cm3/10 min |
ISO 1133 |
| ELECTRICAL |
Value |
Unit |
Standard |
| Volume Resistivity |
1.E+15 |
Ohm-cm |
IEC 60093 |
| Surface Resistivity, ROA |
>1.E+15 |
Ohm |
IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm |
19 |
kV/mm |
IEC 60243-1 |
| Relative Permittivity, 1 MHz |
2.6 |
- |
IEC 60250 |
| Dissipation Factor, 50/60 Hz |
0.004 |
- |
IEC 60250 |
| Dissipation Factor, 1 MHz |
0.001 |
- |
IEC 60250 |
| Relative Permittivity, 50/60 Hz |
2.6 |
- |
IEC 60250 |
| FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
| UL Recognized, 94HB Flame Class Rating (3) |
1.5 |
mm |
UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value (3) |
3 |
mm |
UL 94 |
| Glow Wire Flammability Index 960°C, passes at |
3.2 |
mm |
IEC 60695-2-12 |
| Oxygen Index (LOI) |
19 |
% |
ISO 4589 |