| TYPICAL PROPERTIES1
| TYPICAL VALUE
| Unit
| Standard |
| MECHANICAL |
Tensile Stress, yield, 50 mm/min
| 60
| MPa
| ISO 527 |
| Tensile Stress, break, 50 mm/min
| 55
| MPa
| ISO 527 |
| Tensile Strain, yield, 50 mm/min
| 4.5
| %
| ISO 527 |
| Tensile Strain, break, 50 mm/min
| 30
| %
| ISO 527 |
| Tensile Modulus, 1 mm/min
| 2400
| MPa
| ISO 527 |
| Flexural Stress, yield, 2 mm/min
| 85
| MPa
| ISO 178
|
| Flexural Modulus, 2 mm/min
| 2200
| MPa
| ISO 178
|
| Hardness, H358/30
| 95
| MPa
| ISO 2039-1
|
| IMPACT |
Izod Impact, notched 80*10*4 +23°C
| 20
| kJ/m2
| ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C
| 10
| kJ/m2
| ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
| 20
| kJ/m2
| ISO 179/1eA
|
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
| 10
| kJ/m2
| ISO 179/1eA |
| THERMAL |
Thermal Conductivity
| 0.25
| W/m-°C
| ISO 8302 |
| CTE, 23°C to 60°C, flow
| 8.E-05
| 1/°C
| ISO 11359-2 |
| CTE, 23°C to 60°C, xflow
| 8.E-05
| 1/°C
| ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C
| PASSES
| -
| IEC 60695-10-2
|
| Vicat Softening Temp, Rate A/50
| 245
| °C
| ISO 306 |
| Vicat Softening Temp, Rate B/50
| 190
| °C
| ISO 306 |
| Vicat Softening Temp, Rate B/120
| 195
| °C
| ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
| 185
| °C
| ISO 75/Be |
| Relative Temp Index, Elec
| 120
| °C
| UL 746B |
| TYPICAL PROPERTIES1 |
TYPICAL VALUE |
Unit |
Standard |
| THERMAL |
Relative Temp Index, Mech w/impact |
110 |
°C |
UL 746B |
| Relative Temp Index, Mech w/o impact |
125 |
°C |
UL 746B |
| PHYSICAL |
Mold Shrinkage on Tensile Bar, flow (2) (5)
|
1.6 - 2 |
% |
SABIC Method |
| Density |
1.1 |
g/cm3 |
ISO 1183 |
| Water Absorption, (23°C/sat) |
4.2 |
% |
ISO 62 |
| Moisture Absorption (23°C / 50% RH) |
1.34 |
% |
ISO 62 |
| Melt Volume Rate, MVR at 280°C/1.2 kg |
5 |
cm3/10 min |
ISO 1133 |
| FLAME CHARACTERISTICS |
UL Recognized, 94HB Flame Class Rating (3) |
1.5 |
mm |
UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value (3) |
3 |
mm |
UL 94 |
| PROCESSING PARAMETERS |
TYPICAL VALUE |
Unit |
| Injection Molding |
Drying Temperature |
100 - 120 |
°C |
| Drying Time |
2-3 |
hrs |
Maximum Moisture Content |
0.07 |
% |
| Melt Temperature |
280 - 310 |
°C |
| Nozzle Temperature |
270 - 300 |
°C |
| Front - Zone 3 Temperature |
280 - 300 |
°C |
| Middle - Zone 2 Temperature |
270 - 290 |
°C |
Rear - Zone 1 Temperature |
260 - 280 |
°C |
| Hopper Temperature |
60 - 80 |
°C |
| Mold Temperature |
80 - 120 |
°C |
|
|